201 Stainless Steel Plate
We are the reliable supplier and wholesale of the 201 stainless steel plate/201 stainless steel sheet The characteristic of 201 stainless steel is acid-resisting, alkali-resistance, high density, no bubbles by polishing, no pinhole and etc., It is high-quality material in the production of...
We are the reliable supplier and wholesale of the 201 stainless steel plate/201 stainless steel sheet
The characteristic of 201 stainless steel is acid-resisting, alkali-resistance, high density, no bubbles by polishing, no pinhole and etc., It is high-quality material in the production of various straps and covers.
201 stainless steel sheet , 201 stainless steel plate
JIS, AISI, ASTM, GB, DIN
Standard size : 1000/1219/1250 /1500/1800/2000mm or as the customers' requirements
Standard size :1000/2000/2438/3000/6000mm or as the customers' requirements
NO.1/NO.4/8K/HL/BA/2B/ construction material 4'X8' decorative stainless steel sheet
Cold rolled ,hot rolled
Construction field, ships building industry, petroleum & chemical industries, war and electricity industries, food processing and medical industry, boiler heat ex-changer, machinery and hardware fields ,etc.
Export standard or as customers' requirement
Within 7- 10 working days, according to customers' quantity
High Quality. SGS inspection is accepted if needed
We will supply you good quality, bottom price and first-class service in china and hope to be your golden supplier
Will the 201 stainless steel sheet gathers rust easily?
When the brown rust appeared on 201 stainless steel surface , people may be surprised and think if it gathers rust, it is not stainless steel any more and there is some problem with 201 stainless steel. In fact, this is a misconception of stainless steel because they do not know stainless steel too much.
There is a thin and solid chromium oxide film (protective film) on the cover of stainless steel to prevent the infiltration of oxygen atoms. Once the protective film is destructed by something, the stainless steel will also gather rust. So the surfaces of stainless steel must be cleaned and scrubbed regularly to remove attachments and eliminate external factors that cause corrosion.
Processing and Forming
Type 201 stainless cannot be hardened by heat treatment, but can by cold working.
Type 201 can be annealed at temperatures between 1010 and 1093°C (1850 and 2000°F). In order to keep carbides in solution and avoid sensitization, rapid cooling through the carbide precipitation range 815 and 426°C (1500 and 800°F) is required.
This grade of stainless can be both formed and drawn. Intermediate annealing may be required for severe operations as a result of type 201's high work-hardening rate.